Curable fiberglass binder

ABSTRACT

A curable formaldehyde-free binding composition for use with fiberglass is provided. Such curable composition comprises an addition product of an amine and a reactant to form an amino-amide intermediate. To the amino-amide is added an aldehyde or ketone to form the curable binder composition. The composition when applied to fiberglass is cured to form a water-insoluble binder which exhibits good adhesion to glass. In a preferred embodiment the composition when applied to fiberglass provides a sufficient blackness required in facer products.

BACKGROUND

The subject invention pertains to an improved binding composition for use with fiberglass. More specifically, the invention pertains to an improved curable composition comprising an addition product of an amine and a reactant in the form of a amino-amide intermediate. An aldehyde or ketone is added to the amino-amide to form a composition which upon curing is capable of forming a water-insoluble polymer composition which displays good adhesion to glass. Once applied to the fiberglass, the binding composition is cured. The binder of the present invention is useful as a fully acceptable replacement for formaldehyde-based binders in non-woven fiberglass products, and actually provides a binder exhibiting improved physical properties.

Fiberglass binders have a variety of uses ranging from stiffening applications where the binder is applied to woven or non-woven fiberglass sheet goods and cured, producing a stiffer product; thermo-forming applications wherein the binder resin is applied to a sheet or lofty fibrous product, following which it is dried and optionally B-staged to form an intermediate but yet curable product; and to fully cured systems such as building insulation.

Fiberglass binders used in the present sense should not be confused with matrix resins which are an entirely different and non-analogous field of art. While sometimes termed “binders”, matrix resins act to fill the entire interstitial space between fibers, resulting in a dense, fiber reinforced product where the matrix must translate the fiber strength properties to the composite, whereas “binder resins” as used herein are not fully space-filling, but rather coat only the fibers, and particularly the junctions of fibers. Fiberglass binders also cannot be equated with paper or wood product “binders” where the adhesive properties are tailored to the chemical nature of the cellulosic substrates. Many such resins are not suitable for use as fiberglass binders. One skilled in the art of fiberglass binders would not look to cellulosic binders to solve any of the known problems associated with fiberglass binders.

Binders useful in fiberglass products generally require a low viscosity in the uncured state, yet possess characteristics so as to form a rigid thermoset polymeric binder for the glass fibers when cured. A low binder viscosity in the uncured state is required to allow the mat to be sized correctly. Also, viscous binders commonly tend to be tacky or sticky and hence they lead to the accumulation of fiber on the forming chamber walls. This accumulated fiber may later fall onto the mat causing dense areas and product problems.

From among the many thermosetting polymers, numerous candidates for suitable thermosetting fiberglass binder resins exist. However, binder-coated fiberglass products are often of the commodity type, and thus cost becomes a driving factor, generally ruling out resins such as thermosetting polyurethanes, epoxies, and others. Due to their excellent cost/performance ratio, the resins of choice in the past have been phenol-formaldehyde resins. Phenol-formaldehyde resins can be economically produced, and can be extended with urea prior to use as a binder in many applications. Such urea-extended phenol-formaldehyde binders have been the mainstay of the fiberglass industry for years, for example.

Over the past several decades however, minimization of volatile organic compound emissions (VOCs) and hazardous air pollutants (HAPS) both on the part of the industry desiring to provide a cleaner environment, as well as by Federal regulation, has led to extensive investigations into not only reducing emissions from the current formaldehyde-based binders, but also into candidate replacement binders. For example, subtle changes in the ratios of phenol to formaldehyde in the preparation of the basic phenol-formaldehyde resole resins, changes in catalysts, and addition of different and multiple formaldehyde scavengers, has resulted in considerable improvement in emissions from phenol-formaldehyde binders as compared with the binders previously used. However, with increasingly stringent Federal regulations, more and more attention has been paid to alternative binder systems which are free from formaldehyde.

One such candidate binder system employs polymers of acrylic acid as a first component, and a polyol such as triethanolamine, glycerine, or a modestly oxyalkylated glycerine as a curing or “crosslinking” component. The preparation and properties of such poly(acrylic acid)-based binders, including information relative to the VOC emissions, and a comparison of binder properties versus urea-formaldehyde binders is presented in “Formaldehyde-Free Crosslinking Binders For Non-Wovens,” Charles T. Arkins et al., TAPPI Journal, Vol. 78, No. 11, pages 161-168, November 1995. The binders disclosed by the Arkins article, appear to be B-stageable as well as being able to provide physical properties similar to those of urea/formaldehyde resins.

U.S. Pat. No. 5,340,868 discloses fiberglass insulation products cured with a combination of a polycarboxy polymer, a-hydroxyalkylamide, and at least one trifunctional monomeric carboxylic acid such as citric acid. The specific polycarboxy polymers disclosed are poly(acrylic acid) polymers. See also, U.S. Pat. No. 5,143,582.

U.S. Pat. No. 5,318,990 discloses a fibrous glass binder which comprises a polycarboxy polymer, a monomeric trihydric alcohol and a catalyst comprising an alkali metal salt of a phosphorous-containing organic acid.

U.S. 2007/0142596 discloses binders comprised of a mixture of Maillard reactants. The reactants comprise a monosaccharide and an ammonium salt of a polycarboxylic acid.

Published European Patent Application EP 0 583 086 A1 appears to provide details of polyacrylic acid binders whose cure is catalyzed by a phosphorus-containing catalyst system as discussed in the Arkins article previously cited. Higher molecular weight poly(acrylic acids) are stated to provide polymers exhibiting more complete cure. See also U.S. Pat. Nos. 5,661,213; 5,427,587; 6,136,916; and 6,221,973.

Some polycarboxylic polymers have been found useful for making fiberglass insulation products. Problems of clumping or sticking of the glass fibers to the inside of the forming chambers during the processing, as well as providing a final product that exhibits the recovery and rigidity necessary to provide a commercially acceptable fiberglass insulation product, have been overcome. See, for example, U.S. Pat. No. 6,331,350. The thermosetting acrylic resins have been found to be more hydrophilic than the traditional phenolic binders, however. This hydrophilicity can result in fiberglass insulation that is more prone to absorb liquid water, thereby possibly compromising the integrity of the product. Also, the thermosetting acrylic resins now being used as binding agents for fiberglass have been found to not react as effectively with silane coupling agents of the type traditionally used by the industry increasing product cost. The addition of silicone as a hydrophobing agent results in problems when abatement devices are used that are based on incineration as well as additional cost. Also, the presence of silicone in the manufacturing process can interfere with the adhesion of certain facing substrates to the finished fiberglass material. Overcoming these problems will help to better utilize polycarboxylic polymers in fiberglass binders.

Accordingly, in one aspect the present invention provides a novel, non-phenol-formaldehyde binder.

Another aspect of the invention provides a novel fiberglass binder which provides advantageous flow properties, the possibility of lower binder usage, the possibility of overall lower energy consumption, elimination of interference in the process by a silicone, and improved overall economics.

Still another aspect of the present invention is to provide a binder for fiberglass having improved economics, while also enjoying improved physical properties. In addition, the present invention increases the sustainable portion of the binder and reduces the dependency on a fossil based source for the resin.

These and other aspects of the present invention will become apparent to the skilled artisan upon a review of the following description and the claims appended hereto.

SUMMARY OF THE INVENTION

A curable composition for use in the binding of fiberglass is provided comprising an addition product of an amine and a saturated or unsaturated reactant in the form of an amino-amide intermediate. To this intermediate is added an aldehyde or ketone, preferably a reducing sugar, to form a curable binder composition. This composition upon curing is capable of forming a water-insoluble polymer composition which exhibits good adhesion to glass.

A process for binding fiberglass is provided comprising applying to fiberglass a coating of a composition comprising an addition product of an amine and a saturated or unsaturated reactant in the form of an amino-amide intermediate, to which is added an aldehyde or ketone. Thereafter the composition is cured while present as a coating on the fiberglass to form a water-insoluble polymer composition which exhibits good adhesion to the fiberglass.

In one embodiment, the amino-amide intermediate is first heated to create an oligomer. The aldehyde or ketone is added to the oligomer. This composition is added to the fiberglass as a binder and cured.

In a preferred embodiment the resulting fiberglass product is a fiberglass mat as facer. In other embodiments the fiberglass product is a microglass-based substrate useful when forming a printed circuit board, battery separator, filter stock, or reinforcement scrim.

BRIEF DESCRIPTION OF THE DRAWINGS

Notwithstanding any other embodiments that may fall within the scope of the present disclosure, several embodiments of the present invention will now be described, by way of example, with reference to the accompanying drawings in which:

FIG. 1 is a graph of dry tensile strength of non-woven glass mat bonded with HDMA/MA/Glucose binder.

FIG. 2 is a graph of hot/wet tensile strength of non-woven glass mat bonded with HMDA/MA/Glucose binder.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

The novel fiberglass binder composition of the present invention is a curable composition comprising the reaction product of an amine and a saturated or unsaturated reactant to form an amino-amide intermediate.

In accordance with one embodiment of the invention, amine reactants are selected which are capable of undergoing conjugate addition to form the requisite amino-amide, which forms a water-insoluble polyimide upon curing. In such an embodiment the amine is a di- or multi-functional primary or secondary amine. More preferably, the amine is a diamine having at least one primary amine group.

Preferred examples of amines include, but are not limited to, aliphatic, cycloaliphatic and aromatic amines. The amines may be linear or branched. The amine functionalities may be di- or multifunctional primary or secondary amines. The amines can include other functionalities and linkages such as alcohols, thiols, esters, amides, acids, ethers and others.

Preferred amines that are suitable for use in such an embodiment include 1,2-diethylamine, 1,3-propanediamine, 1,4-butanediamine, 1,5-pentanediamine, 1,6-hexanediamine, .alpha.,.alpha.′-diaminoxylene, diethylenetriamine, triethylenetetramine, tetraethylenepentamine, and mixtures of these. A preferred diamines for use in this embodiment of the invention are 1,4-butanediamine and 1,6-hexanediamine. Natural and synthetic amino acids such as lysine, anginine, hestidine, etc. can also be used.

The curable amino-amide is formed through the selection of an unsaturated or saturated reactant that is an anhydride, carboxylic acid, ester, and salts and mixtures of such reactants. Preferred unsaturated reactants are maleic acid, fumaric acid, maleic anhydride, mono- and di-esters of maleic acid and fumaric acid, and salts and mixtures of these. Ammonium salts of the unsaturated acids of their monoesters conveniently can be utilized. A preferred unsaturated reactant is maleic anhydride. Preferred saturated reactants include, but are not limited to, succinic anhydride, succinic acid, mono and diesters of succinic acid, glutaric acid and anhydride, phthalic acid and anhydride, tetrahydro phthaic acid and anhydride, mono and diesters of acid anhydrides and salts of the acids, and their mono esters. A preferred saturated reactant is phthalic anhydride or tetrahydro phthalic anhydride.

The amino-amide addition products can be readily formed by mixing the components in an aqueous medium at room temperature. The resulting addition products are either water-soluble, water-dispersible, or are present as an emulsion. To the solution of amino-amide, the carbonyl functional materials can be added, especially an aldehyde or ketone. Due to their higher reactivity, aldehydes are preferred to ketones. The composition comprises the amino-amide and the aldehyde and/or ketone. Some reaction does take place within the composition between the components. However, the reaction is completed during the curing step, followed by the cross-linking reaction of curing.

Preferred examples of suitable aldehydes include, but are not limited to, mono- and multifunctional aldehydes including acetaldehyde, hydincy acetaldehyde, butyraldehyde, acrolein, furfural, glyoxal, glyceraldehyde, glutaraldehyde, polyfurfural, polyacrolein, copolymers of acrolein, and others. Reducing mono, di- and polysaccharides such as glucose, celobrose, maltose, etc. can be used, with reducing monosaccharides, such as glucose being preferred. In particular non-cyclic monosaccharides containing a ketone and/or aldehyde functional group and hydroxyl groups on most or all of the non-carbonyl carbon atoms are preferred. Most preferred monosaccharides are Triose (3 carbon atoms), Tetrose (4 carbon atoms), Pentose (5 carbon atoms), Hexose (6 carbon atoms) and Heptose (7 carbon atoms), in particular glucose (dextrose), fructose (levulose), galactose, xylose and ribose. The term monosaccharide includes also the Aldose or Ketose of the aforementioned monosaccharides. A molar ratio of salt to carbonyl (saccharide) can vary, but is generally in the range of from 1:50 to 50:1. A ratio of 1:20 to 20:1 is more preferred, with a ratio of 1:10 to 10:1 being most preferred.

Preferred examples of ketones include, but are not limited to, acetone, acetyl acetone, 1,3-dihydroxy acetone, benzyl, benzoin, fructose, etc.

The aldehydes and ketones react with the amino-amide intermediate, which contains an amic acid function, i.e., an amide linkage in the vicinity of a carboxylic acid. An amic acid function is more reactive than a simple carboxylic acid. The amount of aldehyde and/or ketone added is generally such that the molar ratio of carboxylic acid in the amino-amide to carbonyl or ketone is from 1:5 to 50:1. A ratio of 1:20 to 20:1 is more preferred, with a ratio of 1:10 to 10:1 being most preferred.

One advantage is that the presence of all functional groups, i.e., amine, amide and carboxylic acid, on the same molecule eliminates the potential need for the addition of external crosslinkers or binders such as polycarboxylic acids and/or polyvinyl alcohol. Such crosslinkers can be added, however if desired.

In an embodiment, the amino-amide can be first oligomerized prior to adding the aldehyde or ketone. The amino-amide can be heated until an oligomer is obtained, e.g., a dimer, trimer or tetramer of the amino-amide intermediate. An example of suitable conditions for making the oligomer involves heating in the range of from 120-150° C. for up to 5 hours.

Using the oligomerized product has been found to result in a more robust binder product upon curing. This manifests itself in the strength of the binder, and allows for better storage results, higher tensile strength and rigidity, and better recovery for products made with the binder.

The composition when applied to the fiberglass optionally can include adhesion prompters, oxygen scavengers, solvents, emulsifiers, pigments, fillers, anti-migration aids, coalescent aids, wetting agents, biocides, plasticizers, organosilanes, anti-foaming agents, colorants, waxes, suspending agents, anti-oxidants, crosslinking catalysts, secondary crosslinkers, and combinations of these.

It has been found that in particular curable compositions comprising a thickener and/or rheology modifier provide improved properties, such as improved dry tensile strength and hot/wet tensile strength, of fiberglass mats, as can be seen from Figure 1 and Figure 2.

Examples below shows an improvement in dry tensile strength and hot-wet tensile strength of a non-woven glass mat when a thickener is added to the binder. The binder used is a solution of Hexamethylene diamine, maleic anhydride and glucose. The thickener used is a type of hydroxyl cellulose thickener, Natrosol 250H4BR from Hercules.

The following test method was applied:

Individual 1″×6″ test specimens were cut from fiberglass mats with the LOI of 19% using a paper cutter along both machine direction (MD) and cross-machine direction (CMD). For dry tensile, 12 MD specimens and 12 CMD specimens were tested on the Instron 4466 Test machine with the 100 lb load cell and a crosshead speed of 1 in/min. For hot/wet tensile, 12 MD specimens were immersed in 180° F. water for ten (10) minutes, allowing them to dry for three (3) minutes before testing on Instron Test machine.

The thickener and/or rheology modifier can be polymeric-type materials which are at least partially water soluble or inorganic-type materials that are dispersed in water and which increase the viscosity without substantially modifying the other resin properties. Suitable polymeric thickeners are polysaccharides such as xanthan gum, guar gum, modified starches, neutralized polyacrylic acids, such as sodium polyacrylate, cellulose derivatives, polyacrylamides and polyvinylalcohols. Preferably such thickener and/or rheology modifier have a weight average molecular weight of at least about 100,000 and most typically below about 2,000,000, most preferably of at least about 200,000 and most typically below about 1,000,000. Inorganic thickeners include smectite clay and/or bentonite.

Preferred thickeners are based on hydroxyalkyl cellulose, such as hydroxyethyl cellulose, hydroxypropyl cellulose, hydroxyethyl methyl cellulose, hydroxypropyl methyl cellulose, or carboxyalkyl cellulose, such as carboxymethyl cellulose.

The amount of thickener and/or rheology modifier being present in the curable composition is preferably from 0.01 to 3 weight percent (based on dry mass), most preferably from 0.05 to 0.1 weight percent (based on dry mass).

In addition, it has been found that in particular curable compositions comprising a 10 to 50 weight percent (based on dry mass), most preferably from 20 to 40 weight percent (based on dry mass) of a carbon black dispersion offers excellent blacking performance. The water based carbon black dispersion comprises typically water, 40 to 50 weight percent carbon black, 0.1 to 5 weight percent, preferably 0.1-2 weight percent cationic or non-ionic emulsifiers. The water based carbon black dispersion typically may further comprise other additives such as silanes, de-foamer and wetting agents for glass fibers. Instead of using a water based carbon black dispersion being added to the curable compositions, it is also possible to add the carbon black directly to the curable compositions. This, however, is less preferred for handling reasons. The aforementioned curable compositions comprising carbon black provide sufficient blackness when used in so called facer materials, which are fibrous materials predominately based on glass fibers.

The carbon black preferably has particle size of 70 nm or less, most preferred from 5 nm to 70 nm, in particular from 10 nm to 30 nm. Such carbon black materials are available for example from Brockhuis GmbH & Co KG (Rockwood Pigments NA, Inc).

The fiberglass that has the composition according to the present invention applied to it may take a variety of forms and in a preferred embodiment is Fiberglass mat, preferably facer mats. Use in roofing membranes is also preferable as good tensile and elongation is observed. In other embodiments the fiberglass is a microglass-based substrate useful in applications such as printed circuit boards, battery separators, filter stock, and reinforcement scrim.

The composition of the present invention can be applied to the fiberglass by a variety of techniques like spraying, spin-curtain coating, and dipping-roll coating. In a most preferred embodiment the inventive binder composition is applied to the non-woven using state of the art standard binder application methods as it is widely used in the industry. Water or other solvents can be removed by heating.

Thereafter the composition undergoes curing wherein a polymeric coating is formed which exhibits good adhesion to glass. The polymeric composition obtained upon curing is a combination of a polyamino-amide and a polyamino-imide. The polyimide is the primary product, but some of the amide in the intermediate is believed to not form the imide. Thus, some polyamino-amide is also present in the cured composition/binder.

Such curing can be conducted by heating. Elevated curing temperatures on the order of 100 to 300° C. generally are acceptable. Satisfactory curing results are achieved by using standard heating and drying processes as it is commonly used for the glass fiber mat production. Temperatures of around 200° C. in an air oven at line speed are typically sufficient.

The amount of cured binder at the conclusion of the curing step commonly is approximately 10 to 30 percent by weight, and most preferably 12 to 20 percent by weight of the total weight of the mat.

The inventive binder composition can be applied to all kind of different fibrous substrates. The fibrous substrate can be a woven or non-woven material, and can comprise filaments, chopped fibers, staples fibers or mixtures thereof. Polymer fibers and glass fibers are preferred, however all kind of fiber materials which are compatible with the inventive binder composition can be used.

The inventive composition is particularly advantageous for glass fiber nonwoven used as facer. The intensive black color allows a large variety of different applications. The inventive composition is particularly suitable for facer mats with a total weight between 20 to 200 g/sqm, having a preferred weight range between 40 to 100 g/sqm total mat weight.

The facer mats used in the present invention typically comprises at least one non-woven web bonded together with the inventive binder. The web comprises chopped continuous glass fibers, of which preferably at least about 90 percent, more preferably at least about 95 percent, and most preferably least about 97 percent have a fiber diameter within the range of 1 to 30 μm, most preferred within the range of 7μ to 13μ. For some applications it is preferred to have a very narrow range of about 11±1.5 μm as described it WO2005/005118 which disclosure is hereby entirely incorporated by reference.

Further, it is also possible that the web has several layers of chopped glass fibers, preferably an outer layer of glass fibers having a diameter from 1 to 10 μm and an inner layer of glass fibers having a diameter from 12 to 30 μm. In such case the inner layer provides mechanical strength and the outer layer is aesthetically pleasing. More details about such facer materials can be found in EP-A-1,800,853 which disclosure is hereby entirely incorporated by reference.

In addition, it is also possible that the web comprises of a blend of chopped glass fibers, preferably a major portion of chopped glass fibers have a diameter from 8 to 17 μm while the minor portion of the chopped glass fibers have a diameter of less than about 5.5 μm. The minor portion is typically present in about 1 to 30 weight percent of the dry weight of the web. More details about such facer materials can be found in WO-A-2005/005117 which disclosure is hereby entirely incorporated by reference.

Although mixtures of different lengths of chopped strand fibers are contemplated and included within the scope of the invention, it is most preferred that a majority of the fibers have lengths of about 0.20 inches to 1.5 inches, more preferred from about 0.25 inches to 0.6 inches.

Chopped strand fibers are readily distinguishable from staple fibers by those skilled in the art. Staple fibers are usually made by processes such as rotary fiberization or flame attenuation of molten glass known in the fiber industry. They typically have a wider range of lengths and fiber diameters than chopped strand fibers. By way of contrast, it would have been anticipated that the smoothest mats would be obtained with a preponderance of fine fibers.

A preferred continuous glass fiber for fibrous web is at least one member selected from the group consisting of E, C, T and S type and sodium borosilicate glasses, and mixtures thereof. As is known in the glass art, C glass typically has a soda-lime-borosilicate composition that provides it with enhanced chemical stability in corrosive environments, and T glass usually has a magnesium aluminosilicate composition and especially high tensile strength in filament form. E glass, which is also known as electrical glass typically has a calcium aluminoborosilicate composition and a maximum alkali content of 2.0%. E glass fiber is commonly used to reinforce various articles. The web is preferably composed of C glass or E glass.

If required by the later application, the inventive binder used for the present web may comprise an effective amount of a water repellant, for example, vinyl acrylate latex copolymers or stearylated melamine in typical amounts of about 3 to 10 wt. %.

The web may contain further fillers, pigments, or other inert or active ingredients either throughout the mat or concentrated on a surface. For example, the mat can contain effective amounts of fine particles of limestone, glass, clay, coloring pigments, biocide, fungicide, intumescent material, or mixtures thereof. Such additives may be added for known structural, functional, or aesthetic qualities imparted thereby. These qualities include additional coloration, modification of the structure or texture of the surface, resistance to mold or fungus formation, and fire resistance. Preferably, flame retardants sufficient to provide flame resistance, e.g. according to NFPA Method 701 of the National Fire Protection Association or ASTM Standard E84, Class 1, by the American Society for the Testing of Materials, are added. Biocide is preferably added to the mat to resist fungal growth, its effectiveness being measurable in accordance with ASTM Standard D3273.

Beside the chopped glass fibers, the web may contain a minor portion of other fibers, either in addition to or in replacement of glass fibers, such as mineral fibers, such as mineral wool, slag wool, ceramic fibers, carbon fibers, metal fibers, refractory fibers, or mixtures thereof. Other synthetic or polymer fibers, such as melt blown micro denier fibers or melt spun fibers of polyester, nylon, polyethylene, polypropylene, or the like, may also be used.

The non-woven web used in the facer mat has preferably a total weight ranging from about 20 to 200 g/m², more preferred from 25 to 150 g/m², and most preferred from 30 to 100 g/m².

The present invention provides a formaldehyde-free route to form a securely bound formaldehyde-free fiberglass product. The binder composition of the present invention provides advantageous flow properties, the elimination of required pH modifiers such as sulfuric acid and caustic, and improved overall economics and safety. The binder also has the advantages of being stronger and offering lower amounts of relative volatile organic content during curing, which ensures a safer work place and environment. The cure time of the binder is also seen to be much faster and therefore does favor the economics, while reducing the energy consumption during the curing process and lowering the carbon footprint. The binder also contains a high level of sustainable raw materials further reducing the dependency on fossil based sources for the resin. Also, due to the hydrophobic nature of the binder, the need for water repellant such as silicones is eliminated or greatly reduced.

The following examples are presented to provide specific examples of the present invention. It should be understood, however, that the invention is not limited to the specific details set forth in the Examples.

EXAMPLE 1

A binder composition was prepared using the following constituents:

dry dry mass mass total component [%] [%] 73.95 kg binder G4.5 35 73.95 0.7 kg Lutensol ® 50 1 M7 6.26 kg Water 0 19.02 kg Carbofin ® 46 25 L2951 0.0175 kg defoamer 100 0.05

EXAMPLE 2

A binder composition was prepared with the following components:

72.95 kg binder G4.5 35 72.95 0.7 Lutensol ® 50 1 kg M7 6.56 kg Water 0 19.02 kg Carbofin ® 46 25 L2951 0.7 kg Silquest ® 50 1 A1100 0.0175 g defoamer 100 0.05 Binder G4.5 comprises the following components: 30.1% Water soft, 6.2% HMDA (70%) (1,6-Diaminohexane), 3.7% Maleic anhydride, 57.0% Dextrose (71% liquid), 2.4% Ammonium sulfate, 0.4% Skane M8 ® (Rohm&Hass), 0.2% Copper sulfate pentahydrate, percentages based on total weight of binder G4.5. Lutensol ® M7 (BASF) is a non-ionogenic tenside, Carbofin ® L2951 (Rockwood Pigment NA, Inc) is a carbon black emulsion; Silquest ® A1100 is an amino-silane.

The composition was applied to a 60 g/m² glass fiber nonwoven. The binder content was 16% based on the total mat weight. 

That which is claimed is:
 1. A curable composition for use in the binding of fiberglass comprising: an aldehyde or ketone; an amino-amide which is a conjugate addition product of an amine and a reactant; and a thickener, wherein: the amine comprises 1,6-hexanediamine, the reactant comprises maleic anhydride, the aldehyde or ketone comprises a reducing sugar, the amino-amide is oligomerized by heating at a temperature from 120° C. to 150° C. prior to adding the aldehyde or ketone to the amino-amide, and the curable composition is formaldehyde-free.
 2. The curable composition of claim 1, wherein the thickener is based on polysaccharides.
 3. The curable composition of claim 1, wherein the thickener has a weight average molecular weight of at least about 100,000 and below about 2,000,000.
 4. The curable composition of claim 1, wherein the thickener is based on hydroxyalkyl cellulose or carboxyalkyl cellulose.
 5. The curable composition of claim 1, wherein the thickener is present in the curable composition from 0.05 to 0.7 weight percent (based on dry mass).
 6. The curable composition of claim 1, wherein the composition comprises carbon black.
 7. The curable composition of claim 1, wherein the carbon black is present in the curable compositions from 10 to 50 weight percent (based on dry mass).
 8. The curable composition of claim 6, wherein the carbon black has particle size of 70 nm or less.
 9. The curable composition of claim 1, wherein an aldehyde is used with the amino-amide.
 10. The curable composition of claim 1, wherein the amino-amide is an oligomer.
 11. The curable composition of claim 1, wherein: the amino-amide comprises an amide group and a carboxylic acid group, and the amide group and the carboxylic acid group are formed by an amine group of the 1,6-hexanediamine covalently bonding with a carbonyl group of the maleic anhydride.
 12. The curable composition of claim 1, wherein the amino-amide is a monomer, dimer, trimer, or tetramer.
 13. The curable composition of claim 1, wherein the amino-amide comprises an amic acid function. 